Huntsman Uralane® 2-Component Polyurethane Adhesive, Beige/Off-White (Part C/A), 1 qt

Uralane® 5774-A/C polyurethane adhesive is a two component, self-extinguishing material that cures at room or elevated temperature to form tough, impact-resistant bonds to thermoplastics or metal substrates. The mixed compound is a soft paste for application to vertical or overhead surfaces. Cure may be accelerated at moderate temperature (150 to 200 degrees F) for faster production schedules. This product is available in easy-to-use Accumix cartridges for quick, convenient application. Uralane® 5774-A/C polyurethane adhesive is qualified to BMS 5-105, type 5.
Features
• High strength
• Self-extinguishing
• High peel strength
Technical Information
• BMS 5-105, Type 5
Specifications
• Container Size: 1 qt
• Color: Beige/Off-White (Part C/A)
• Composition: 30 to 60% Oxirane, Methyl-, Polymer with Oxirane, Ether with 1,2,3-Propanetriol (3:1), Polymer with 1,1'-Methylenebis[4-Isocyanatocyclohexane], 13 to 30% 1,6,7,8,9,14,15,16,17,17,18,18-Dodecachloropentacyclo[12.2.1.16,9.02,13.05,10]Octadeca-7,15-Diene, 13 to 30% 2-Oxepanone, Polymer with 1,1'-Methylenebis[4-Isocyanatocyclohexane] and 2,2'-Oxybis[Ethanol], 1 to 3% 4,4'-Methylenedicyclohexyl Diisocyanate (Part A), 13 to 30% 4,4'-Methylenebis(2-Ethylaniline), 7 to 13% Tris(Methylphenyl) Phosphate, 3 to 7% Formaldehyde, Polymer with 2-Ethylbenzenamine, 3 to 7% 4,4'-Methylenebis[N-Sec-Butylaniline], 1 to 3% 2-Ethylaniline, 1 to 3% 1,1',1'',1'''-Ethylenedinitrilotetrapropan-2-Ol, 0.1 to 1% Ethylbenzene (Part C)
• Flash Point: 202 deg C (Part A), >100 deg C (Part C)
• Curing Time: 7 days at Room Temperature
• Density: 1.32 g/cc (Part A), 1.15 to 1.4 g/cc (Part C)
• Mixing Ratio: 100:55
• Form: Liquid
• Viscosity: 20 to 35000 cP (Part A)
• Specific Gravity: 1.1 (Part A), 1.2 (Part C)
• Odor/Scent: Slight (Part A), Amine-Like (Part C)
• Shelf Life: 6 months
• Setting Time: 15 to 25 min
• Base Type: Polyurethane
• Shear Strength: 220 to 2080 psi at 2 to 168 hr at 77 deg F
• Vapor Pressure: <1 hPa
• Solubility: Insoluble