P/S 890 Class B is a two-part, manganese dioxide-cured polysulfide compound designed for fillet sealing of integral aircraft fuel tanks. It is ideal for sealing fuel tanks and other aircraft fuselage applications.
Don't have an account? Register for an account here.
WARNING: This product can expose you to chemicals including CARBON BLACK (AIRBORNE, UNBOUND PARTICLES OF RESPIRABLE SIZE [= 10 MICROMETERS]), TITANIUM DIOXIDE (AIRBORNE, UNBOUND PARTICLES OF RESPIRABLE SIZE) and TOLUENE which is [are] known to the State of California to cause cancer and birth defects or other reproductive harm. For more information go to www.P65Warnings.ca.gov.
Overview
The uncured material is a low sag, thixotropic paste suitable for application by extrusion gun or spatula. It cures at room temperature to form a resilient sealant with excellent adhesion to common aircraft substrates. The cured sealant maintains excellent elastomeric properties after prolonged exposure to both jet fuel and aviation gas. It has a service temperature range from -65°F (-54°C) to 250°F (121°C), with intermittent excursions up to 275°F (135°C). The B-2 classification indicates a specific two-hour work life (application life) after mixing, making it suitable for applications requiring more time than faster-curing variants. The storage life of P/S 890 Class B is at least 9 months when stored at temperatures below 80°F (27°C) in original, unopened containers.
Features & Benefits
Thermal rupture resistance for reliable performance
Low temperature flexibility to maintain seal integrity
Corrosion resistance
Flexibility with no cracks after bending 180 degrees over a 0.125 inch (3.18 mm) mandrel
Resistance to hydrocarbons
Repairable to itself, excellent for both freshly cured and fuel-aged fillets
Outstanding resistance to water, alcohols, and petroleum-based fluids
Fungus resistant - non-nutrient
Specifications
Color: Part A - Black, Part B - White, Mixed - Gray
Mixing Ratio by Weight: Part A: Part B 10:100
Base Viscosity: 11,000 (1100) (Brookfield #6 @ 10rpm), Poise (Pa-s)
Application Life @ 77°F (25°C), 50% RH: 2 hrs
Cure Time: 14 days @ 77°F (25°C), 50% RH
Cured Specific Gravity: 1.55
Nonvolatile Content: 95%
Tensile Strength: 300 psi (2069 KPa) - Standard cure, 14 days @ 77°F (25°C), 50% RH
Elongation: 300% - Standard cure, 14 days @ 77°F (25°C), 50% RH