PAINT: EPOXY,CLR,2 LTR, EPOXY KIT,BASE & CATLYST

The IP9064 system of coating is a combination of three systems, which can be used individually or all three for total maximum protection. Each of the three individual 'layers' are stand alone products in their own right.
Features
• Pre-treatment etch (or wash) primer - a two part pre-treatment acid-based primer with filiform corrosion resistance for suitability prepared substrates, it chemically pre-treats the surface to provide maximum adhesion and corrosion resistance, suitable for use with synthetic, 2 pack epoxy, PU primer and a wide range of finishes
• Epoxy strontium chromate primer - a two part corrosion inhibitive epoxy resin-based primer-resistant to all normal aircraft operating fluids, resistant to filiform corrosion if used over pre-treatment etch (or wash) primer, it is suitable for indoor or outdoor use and over-coatable with various epoxy, acrylic and PU topcoats
• Two part air drying epoxy finishers - A two part air drying epoxy finish for interior and exterior use, used by Rolls Royce as both a decorative and protective coating e.g. matt black on fan frame composite castings and an air drying marking paint, this range will probably be increased to comply with customer demand
• Resistant to abrasion, corrosion and most aircraft operating fluids and chemical, this range is also used for painting instruments and touching up our Textron gray stoving and Pratt and Whitney Canada stoving systems
Specifications
• Container Size: 2 L
• Form: Liquid
• Dry Time: 2 to 3 hr (Dry), 16 to 24 hr (Hard Dry)
• Odor/Scent: Characteristic
• Density: 1.02 to 1.4 kg/L
• Relative Density: 1.03 to 1.3
• Shelf Life: 12 months
• Viscosity: 70 to 100 s ISO5 at 23 deg C
• VOC Content: 400 to 480 g/L
• Coverage Area: 10 to 12 sq-m/L
• Application Method: Spray, Brush
• Boiling Point: 124 to 128 deg C
• Base Type: Epoxy Polyurethane
• Flash Point: 24 to 26 deg C
• Composition: 5 to 10% 1-Methoxy-2-Propanol, 10 to 20% Butyl Acetate, 1 to 2% Diacetone Alcohol, 40 to 60% Phenol,4,4'-(1-Methylethylidene)Bis-Polymer with 2,2'-((1-Methylethylidene) Bis (4,1-Phenylene Oxymethylene)) Bis(Oxirane), 20 to 30% Xylene
• Color: Clear