Scotch-Weld™ RP-2110 Repair Paste Kit, Cartridge, 485 mL, Paste, Black, Slight

Our 3M™ Scotch-Weld™ Repair Paste 2110 is also available for purchase on its own or in a kit format. The kit includes, but is not limited to, RP 2110 repair paste in 50 mL Duo-Pak cartridges with a 1:1 mix ratio, 3M™ EPX Applicator Gun, a 3-foot roll of polyester release liner, 3M™ Polyester Tape 8403 Green, a centrifuge tube and 3M™ Single Step Primer 08682. The Duo-Pak cartridges are designed for use with our 3M™ EPX™ applicator system for fast, clean application, leaving you with a portable, easy-to-apply system. The results are a durable protective surface that provides powerful protection year after year. This system makes it suitable to repair polyurethane coatings or films commonly used for erosion protection on aircraft, including helicopter rotor blades, leading edges, engine components and other areas susceptible to erosion damage, especially from sand or rain. Our two-part polyurethane paste enables on aircraft repairs no vacuum bagging required. It can be cured at room temperature in as few as 6 hours or accelerated to 40 min using a heat blanket at a temperature of 140 deg F. Repairs are easy-to perform and yield a smooth, even appearance when complete. With a 10 min work-life, 3M Scotch-Weld™ Repair Paste 2110 provides ample time for working product into the repair area. It is tack-free, flyable and fully cured in less than 24 hours. The finished product has a flat black luster when cured in contact with the textured side of the release liner. The smooth side of the liner provides a glossy luster.

FEATURES
• Helps reduce aircraft on ground (AOG) time and total cost can be applied directly to repair damaged areas of 3M™ polyurethane protective tape
• In-place reparability helps reduce waste and downtime
• Duo-Pak cartridges eliminate the need for weighing and hand-mixing
• No intentionally added solvent in composition helps reduce shrinkage and rework
• Urethane designed for erosion-resistance even in the harshest conditions, including rain and sand erosion
• Suitable for repair of 3M Polyurethane Protective Tape and other protective tapes used on aircraft and engine components
• Convenient 50 mL Duo-Pak Cartridges for easy application with minimal waste

TECHNICAL INFORMATION
• OSHA Approved

SPECIFICATIONS
• Container Size: 485 mL
• Container Type: Cartridge
• Color: Black
• Composition: 70 to 90% Polyurethane Prepolymer, 10 to 15% Methylenebis(4-cyclohexyl Isocyanate), 3 to 4% Hexamethylene Diisocyanate Polymer (Part A), 55 to 85% Polyurethane Prepolymer, 5 to 25% Poly(tetramethylene Ether), <=5% 1, 4-butanediol, <5% Bis(1, 2, 2, 6, 6-pentamethyl-4-piperidinyl) Sebacate, <5% Carbon Black, <5% Phenol, 2-(2h-benzotriazol-2-yl)-6-dodecyl-4-methyl-branched and Linear, <=5% Zeolites, <1% Methyl 1, 2, 2, 6, 6-pentamethyl-4-piperidinyl Sebacate
• Boiling point: >=186 deg C (Part A), >=179 deg C (Part B)
• Flash Point: >=367 deg F (Part A), >=354 deg F (Part B)
• Form: Paste
• Odor/Scent: Slight
• Shelf Life: 365  Days
• Specific Gravity: 1.05
• Viscosity: 190000 to 270000 cPs (Part A), 60000 to 90000 cPs (Part B)
• Density: 1.05 g/mL
• Suitable for Use With: 3M™ Polyurethane Protective Tape 8734NA and 8730NA, Plus a Wide Variety of Urethane Films and Coatings
• Domestic/Import: Domestic

APPLICATIONS
• Helicopter Rotor Blades
• Leading Edges and Engine Components Applications