Scotch-Weld™ 87250003297 Urethane Adhesive, Metals and Plastic, 5 to 15 min, 200 mL Container, 24 hr

We developed 3M™ Scotch-Weld™ urethane adhesive EC-3532 B/A as a fast acting, two-part urethane adhesive which cures at room temperature or with heat to form tough, impact-resistant structural bonds. Our adhesive offers strong adhesion on metals, plastics, composites and many primed or painted metal and plastic substrates. It also becomes non-sag approximately 30 sec after mixing. 3M™ Scotch-Weld™ urethane adhesives EC 3532 B/A creates strong impact-resistant bonds and is engineered to be sag-resistant approximately 30 sec after mixing so the adhesive doesn't run, drip or migrate. Its 5 to 15 min work life allows ample time for handling, accurate application and positioning of parts. EC 3532 B/A forms a fast, secure bond between parts for desired results. To help keep your processes moving forward, 3M™ Scotch-Weld™ urethane adhesive EC 3532 B/A cures in 24 hr at room temperature or sooner with heat. This option gives you control over the speed in which the bond reaches the shear strength required. And to meet various application methods and other needs, Scotch-Weld™ EC 3532 B/A can be applied using a spatula, trowel or flow equipment.

Features
• Eliminating the need to damage surfaces (i.e. drilling holes)
• Joining dissimilar materials and works well with many surfaces
• Producing aesthetically pleasing results as refinishing steps are not required
• Good environmental and chemical-resistance
• Delivers excellent temperature and solvent-resistance
• Does not need access to air or moisture to dry and therefore has an unlimited depth of cure
• Excellent adhesion to many primed or painted metal and plastic substrates minimizes prep

Specifications
• Series: EC3532 B/A
• Container Size: 200 mL
• Container Type: Mix Pack Cartridge
• Color: Brown (Part-A)/Off-White (Part-B)
• Form: Liquid (Part-A/B)
• Odor/Scent: Slight (Part-A), Polyester (Part-B)
• Composition: 30 to 60% Urethane Prepolymer, 10 to 30% Polymethylene Polyphenylene Isocyanate, 10 to 30% Talc, 1 to 10% Diphenylmethane Diisocyanate (MDI), <5% Silica, <1% Sodium Oxide (Part-A), 30 to 60% Polyester Resin, 10 to 30% Talc, 10 to 30% Polypropylene Glycol, 3 to 7% PolyoxyPropylene Triol, <5% Silica, 1 to 5% Zeolites, <2.5% O-Diethylbisaniline, <1% Hydrogenated Castor Oil, <0.99% PM Acetate, <0.5% 2-Ethylhexanoic Acid, <0.5% Sodium Oxide, <0.22% DiButyltin Bis (2-Ethylhexyl Mercaptoacetate) (Part-B)
• Flash Point: >=357 deg F (Part-A), >=354 deg F (Part-B)
• Boiling Point: >=186 deg C (Part-A), >=179 deg C (Part-B)
• VOC Content: 11.4 g/L (Part-B)
• Specific Gravity: 1.34 (Part-A), 1.31 (Part-B)
• Viscosity: 15000 to 32000 cPs (Part-A), 10000 to 40000 cPs (Part-B)
• Shelf Life: 12 months
• Temperature Rating: 60 to 80 deg F
• Applicable Materials: Metals and Plastic
• Shear Strength: 700 psi
• Curing Time: 24 hr
• Mixing Ratio: 100 Accelerator (By Volume), 109 Accelerator (By Weight) (Part-A), 100 Base (By Volume, By Weight) (Part-B)
• Application Time: 5 to 15 min
• Domestic/Import: Domestic

Applications
•Defense
•Facilities Management
•Composite Bonding
•Ducting Bonding
•Metal Bonding
•Vinyl Edge Strip Bonding